附着力促进剂对光固化金属涂层附着力提升的研究

doi:10.12020/j.issn.0253-4312.2020.8.21

涂料工业 ›› 2020, Vol. 50 ›› Issue (8): 21-27. doi: 10.12020/j.issn.0253-4312.2020.8.21

附着力促进剂对光固化金属涂层附着力提升的研究

张嘉琪¹,罗静^*1,刘仁¹,戴胜华²

1.江南大学化学与材料工程学院，江苏无锡 214000； 2.无锡市爱邦特种电线有限公司，江苏无锡 214000

收稿日期:2020-03-03 修回日期:2020-07-06 出版日期:2020-08-01 发布日期:2020-08-01
通讯作者: 罗静 E-mail:jingluo19801007@126.com

Study on Adhesion Enhancement of Adhesion Promoter for UV-Curable Coatings on Metals

Zhang Jiaqi¹，Luo Jing¹，Liu Ren¹，DaiShenghua²

1. School of Chemistry and Materials Engineering，Jiangnan University，Wuxi，Jiangsu 214000，China；
2. Wuxi Aibang Special Wire Co.， Ltd.， Wuxi，Jiangsu 214000，China

Received:2020-03-03 Revised:2020-07-06 Online:2020-08-01 Published:2020-08-01

摘要/Abstract

摘要： 为了探究附着力促进剂对光固化金属基涂层附着力的影响，本文通过划格法、拉拔法及搭接剪切实验，系统研究了磷酸酯类附着力促进剂、硅烷偶联剂对光固化金属基（低碳钢、铝板）涂层附着力的促进作用。结果表明：磷酸类附着力促进剂能够显著提高光固化金属基（低碳钢、铝板）涂层的附着力，而硅烷偶联剂对光固化金属基（低碳钢、铝板）涂层的附着力无明显提升作用。

关键词: 光固化金属基涂层, 磷酸酯类附着力促进剂, 硅烷偶联剂, 低碳钢板, 铝板

Abstract: In order to explore the effects of adhesion promoters on UV-curable coatings on metal substrates，this paper systematically studied the enhancement of the commonly used commercial adhesion promoters（phosphate ester and silane coupling agents）on the adhesion between UV-cured coatings and different metal substrates（mild steel，aluminum plate）by using various test methods，including the cross-cut，pull-off and lap shear tests to clarify the effect of adhesion promoter on the adhesion of UV-curable metal coatings. The results showed that the adhesion of UV-curable metal coatings was significantly improved by the phosphate ester，while the silane coupling agent indicated no remarkable effect.

Key words: UV-curable metal coatings, phosphate adhesion promoter, silane coupling agent, mild steel plate, aluminum plate

中图分类号:

TQ637.83

张嘉琪, 罗静, 刘仁, 戴胜华. 附着力促进剂对光固化金属涂层附着力提升的研究[J]. 涂料工业, 2020, 50(8): 21-27.

Zhang Jiaqi, Luo Jing, Liu Ren, DaiShenghua. Study on Adhesion Enhancement of Adhesion Promoter for UV-Curable Coatings on Metals[J]. Paint & Coatings Industry, 2020, 50(8): 21-27.

https://www.cn-pci.com/CN/Y2020/V50/I8/21

参考文献

[1]ANGDTC，GAN S N.Novel approach to convert non-selfdrying palm stearin alkyds into environmental friendly UV curable resins[J].Progress in Organic Coatings, 2012, 73(4):409-414
[2]庞正智，林晓东.光固化涂层相对内应力与体积收缩率的研究[J].北京化工大学学报, 1995, (44):22-26
[3]祁元春 .紫外光固化脂环族聚氨酯丙烯酸酯涂膜的合成及其改性研究 [D].上海：华东理工大学， 2014.
[4]王雷，孙杰，安成强，等.粗糙度对彩色涂层与基体间附着力的影响[J].电镀与精饰, 2010, 32(5):41-43
[5]WANGQY，BEHNAMIAN Y，LUO H，et al. Anticorrosion performance of chromized coating prepared by pack cemen-tation in simulated solution with H2S and CO2[J].[J].Applied Surface Science, 2017, 419:197-205
[6]王锋，涂伟萍.异氰酸酯改性环氧丙烯酸酯的合成与性能[J].涂料工业, 2009, 39(10):25-29
[7]马子淇，刘伟区，高南，等.有机硅树脂的紫外光固化及其固化膜性能研究[J].涂料工业, 2013, 43(10):26-31
[8]FERTIER L，IBERT M，BUFFE C，et al. New biosourced UV curable coatings based on isosorbide[J].[J].Progress in OrganicCoatings, 2016, 99:393-399
[9]张启禄，王汉锋，谢亚飞，等.紫外光( UV)固化体系附着力促进剂[J].广东化工, 2014, (21):94-95
[10]王征粹.附着力促进剂[J].上海涂料, 1995, (2):57-59
[11]刘国杰 .有机硅附着力促进剂开发与应用的进展（Ⅱ）[J]. 2006，9（12）：13-18.
[12]陈奠宇，徐斌，高飞，等.通用型附着力促进剂的设计、合成与应用[J].广东化工, 2012, (7):36-49
[13]曾光明，陈能昌，王韬.紫外光固化涂料附着力促进剂的研制[J].中国涂料, 2009, 24(8):35-37
[14]李本祥，罗启枚，凌立志，等 .乙二醇二缩水甘油醚双甲基丙烯酸酯磷酸酯及其合成方法 . CN103145755[P]. 2013-06-12.
[15]钟荆祥，程绍楠，王鹏，等.金属用紫外光固化涂料的研发[J].上海涂料, 2011, (12):16-19
[16]谢林， FREYTAG A，MUTH M.重防腐涂料用新型附着力促进剂[J].电镀与涂饰, 2011, (12):58-62
[17]SEO S，LEE D W，AHN J S，et al.Significant performanceenhancement of polymer resins by bioinspired dynamicbonding[J].Advanced Materials, 2017, 29(39):1703026-
[18]CROBU M，ROSSI A，MANGOLINI F，et al.Chain-length-identification strategy in zinc polyphosphate glasses bymeans of XPS and ToF-SIMS[J].Analytical and Bioanalytical Chemistry, 2012, 403(5):1415-1432
[19]BOONAERT C J P，ROUXHET P G.Surface of lactic acid bacteria：relationships between chemical composition andphysicochemical properties[J].Applied and EnvironmentalMicrobiology, 2000, 66(6):2548-2554
[20]LIASCUKIENE I，BEN SALAH M，SABOT R，et al. Deciphering the role and nature of phosphate species at the surface of stainless steel immersed in phosphoric acid solutions[J].[J].Applied Surface Science：A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials, 2018, 434:561-572
[21]MANGOLINI F，ROSSI A，SPENCER N D.Influence of metallic and oxidized ironsteel on the reactivity of triphenyl phosphorothionate in oil solution[J].Tribology International, 2011, 44(6):670-683
[22]SHIMAMURA A，KANEZAKI E，JONES M I，et al. Direct observation of grafting interlayer phosphate in Mg Al layered double hydroxides[J].[J].Journal of Solid State Chemistry, 2012, 186:116-123
[23]SHIN E W，HAN J S，JANG M，et al.Phosphate adsorption on aluminum-impregnated mesoporous silicates：surface structure and behavior of adsorbents[J].Environmental Science & Technology, 2004, 38(3):912-917
[24]杜慧翔，黄活阳，王文鹏，等.硅烷偶联剂的偶联作用机理及其在密封胶中的应用[J].化学与粘合, 2013, 35(2):63-65
[25]晨光化工研究院有机硅编写组 .有机硅单体及聚合物 [M]. 北京：化学工业出版社， 1986：430.

选择文件类型/文献管理软件名称

选择包含的内容

附着力促进剂对光固化金属涂层附着力提升的研究

Study on Adhesion Enhancement of Adhesion Promoter for UV-Curable Coatings on Metals

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	丁振杰, 安晓伟, 何利娜, 等. 有机聚硅氮烷复合涂层的制备及耐高温性研究[J]. 涂料工业, 2025, 55(7): 27-33.
[2]	曹洁, 朱志平, 石西尧, 等. 改性玄武岩鳞片在氟碳重防腐涂料中的应用[J]. 涂料工业, 2023, 53(6): 39-45.
[3]	张家辉, 金玉红, 贾梦秋. 石墨烯-Al₂O₃复合材料的制备及其防腐性能研究[J]. 涂料工业, 2022, 52(11): 1-8.
[4]	李灿刚, 王桂刚, 王德威, 王伟, 邵春妍, 温喜梅, 王华进. 硅烷偶联剂改性云母粉及其在聚脲阻尼材料中的应用[J]. 涂料工业, 2022, 52(10): 8-13.
[5]	李跃, 邱藤, 郭隆海, 叶俊, 何立凡, 李效玉. 用光学微流变研究硅烷偶联剂改性乳胶的流变性及稳定性[J]. 涂料工业, 2021, 51(2): 35-41.
[6]	孙鹏, 董劲, 黄惠, 何亚鹏, 陈步明,. 附着力促进剂对铝阴极板表面环氧涂层性能的影响[J]. 涂料工业, 2021, 51(12): 14-21.
[7]	杨波, 李爽, 张双红, 李茂东, 翟伟, 朱志平. 不同偶联剂对复合纳米导电涂料性能的影响研究[J]. 涂料工业, 2020, 50(6): 1-6.
[8]	李春涛, 吉国强, 叶小机, 王美淑, 陈俊, 张译方. 以复配硅烷偶联剂为基料的无铬锌铝涂层的制备及性能研究[J]. 涂料工业, 2020, 50(3): 21-25.
[9]	赵法强 , 黄强华 , 董晓乐 , 蔡志国 , 杨涛. 硅烷偶联剂改性单组分室温硫化硅橡胶涂覆层对界面性能的影响和效应分析[J]. 涂料工业, 2020, 50(10): 21-26.
[10]	俞传永, 陈磊, 李红轩, 周惠娣, 陈建敏. 八氨基倍半硅氧烷改性聚酰胺酰亚胺基润滑涂层的性能研究[J]. 涂料工业, 2019, 49(5): 8-15.
[11]	周婕, 陈来, 王坤, 汪承磊. 高阻尼性涂层用苯丙乳液的制备与性能研究[J]. 涂料工业, 2017, 47(10): 23-28.
[12]	向美苏, 李非, 张延宗,. 溶胶凝胶法制备甲基三甲氧基硅烷-γ-(2，3- 环氧丙氧) 丙基三甲氧基硅烷复合超疏水涂层[J]. 涂料工业, 2017, 47(1): 1-5.
[13]	王海波, 李楚璇, 杜宗良, 成煦. 氨基硅烷偶联剂对改性水性聚氨酯胶膜性能的影响[J]. 涂料工业, 2016, 46(8): 47-52.
[14]	冉浩, 高伟峰. 汽车用钢铝混线前处理问题对策[J]. 涂料工业, 2016, 46(4): 78-81.
[15]	刘苏静１, ４, 马星１, ４, 栾永胜２, 孙秀敏１, 王建华１, 周晓群３, 隋学会３, 马宣宣１, ４, 夏传海１. KH-570 改性纳米 TiO₂复合丙烯酸防污涂料性能研究[J]. 涂料工业, 2015, 45(7): 14-18.

模态框（Modal）标题

选择文件类型/文献管理软件名称

选择包含的内容

附着力促进剂对光固化金属涂层附着力提升的研究

Study on Adhesion Enhancement of Adhesion Promoter for UV-Curable Coatings on Metals

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价