摘要： 针对阻隔性能优异的聚氯代对二甲苯薄膜(PC膜)的修复研制了氟树脂涂料。通过对氟树脂、真溶剂、助溶剂以及真溶剂和助溶剂的比例对涂料状态及其成膜性能的影响研究，确定了它们在涂料中的合理配比。检测表明其性能达到了相应的技术要求。
关键词:
聚氯代对二甲苯薄膜,
氟碳涂料,
溶剂
Abstract: In this paper, the F, fluorocarbon coatings was developed for repair of the parylene C film with good impermeability. The composition of F resin, true solvent, cosolvent and their ratio on state and film forming property of coating were studied. Test results showed that all the properties completely conform to relevant technical specifications.
Key words:
parylene C film,
F23u4 resin,
coatings,
solvents
李迎军, 周元林, 刘 剑, 吴晓华, 唐贤臣. 聚氯代对二甲苯薄膜用常温固化氟碳涂料的制备[J]. 涂料工业, 2010, 40(4): 40-42.
Li Yingjun, Zhou Yuanlin, Liu Jian, Wu Xiaohua, Tang Xianchen. Preparation of F2314 Resin Based Room Temperature Cured Fluorocarbon Coatings for Parylene C Film[J]. Paint & Coatings Industry, 2010, 40(4): 40-42.