Preparation and Properties of PANI-DBSA/EA/PU Interpenetrating Networks of Conductive Films

doi:10.12020/j.issn.0253-4312.2018.2.25

Abstract

Abstract:

The PANI-DBSA is synthesized by doped reaction of aniline and dodecylbenzenesulfonic acid (DBSA) in epoxy acrylic resin by in-situ emulsion polymerization. PANI-DBSA/EA polymer blends had been mixed with castor oil polyurethane (PU) prepolymer, crosslinking agent (e.g., styrene and acrylonitrile) at the presence of benzoyl peroxide (BPO) as initiator to form the conductive nano-PANI-DBSA/EA/PU interpenetrating networks composite film. By determining the conductivity and tensile strength, the influence of PANI-DBSA content, crosslinking agent, coupling agent and the type and amount of BPO concentration on the conductivity and mechanical properties of the composite film had been studied. The results showed that the composite film exhibited its electrical conductivity up to 2×10 ^-5 S/m and tensile strength 15.8 MPa when it comprised PANI-DBSA 12.5%, KH-550 3%、BPO 0.4% and styrene 60%.

Key words: nano-PANI-DBSA, polyurethane prepolymers, composite films, conductivity, mechanical property

摘要：

用原位乳液聚合法在环氧丙烯酸树脂(EA)中合成了十二烷基苯磺酸掺杂的纳米聚苯胺(PNAI-DBSA),纳米PNAI-DBSA/EA混合物与蓖麻油聚氨酯(PU)预聚体、交联剂(苯乙烯、丙烯腈)等混合后,在引发剂过氧化苯甲酰(BPO)的作用下形成了纳米PANI-DBSA/EA/PU互穿网络导电复合膜。通过测定电导率和拉伸强度,研究了PANI-DBSA含量、交联剂及偶联剂的种类和用量以及BPO用量对复合膜导电和力学性能的影响。结果表明:在PANI-DBSA含量为12.5%、苯乙烯含量为60%、KH-550用量为3%、BPO用量为0.4%时,复合膜的电导率达2×10 ^-5 S/m,拉伸强度为15.8 MPa。

关键词: 纳米聚苯胺, 聚氨酯预聚体, 复合膜, 导电性能, 力学性能

CLC Number:

TQ637.1

Zheng Xin,Mu Zhang,Tan Xiaoming. Preparation and Properties of PANI-DBSA/EA/PU Interpenetrating Networks of Conductive Films[J]. Paint & Coatings Industry, 2018, 48(2): 25-29.

郑鑫,母章,谭晓明. 纳米PANI-DBSA/EA/PU互穿网络导电膜的制备及其性能[J]. 涂料工业, 2018, 48(2): 25-29.

/ / Recommend / Download Citations

URL: https://www.cn-pci.com/EN/10.12020/j.issn.0253-4312.2018.2.25

https://www.cn-pci.com/EN/Y2018/V48/I2/25

References

[1]	吕秋丰, 黄美荣, 李新贵 . 聚苯胺/聚合物透明导电复合膜研究进展[J]. 化工新型材料, 2007,35(3) 28-35.
[2]	CAI Z H, MAITIN C R . Electronically conductive polymer fibers with mesoscopic diameters show enhanced electronic conductivities[J]. Journal of the American Chemical Society, 1989,111(11):4138-4139.
[3]	BANERJEE P, MANDAL B M . Conducting polyaniline nanoparticle bends with extremely low percolation thresholds[J]. Macromolecules, 1995,28(11):3940-3943.
[4]	PALANIAPPAN S, JOHN A . Polyaniline materials by emulsion polymerization pathway[J]. Progress in Polymer Science, 2008,33(7):732-758.
[5]	郑鑫, 谭晓明, 徐闫 , 等. 苯胺在环氧丙烯酸树脂中的原位乳液聚合及性能研究[J]. 化工新型材料, 2013,41(6):66-68.
[6]	JEON B H, KIM S, CHOI M H , et al. Synjournal and characterization of polyaniline—polycarbonate composites prepared by an emulsion polymerization[J]. Synthetic Metals, 1999,104(2):95-100.
[7]	CHANG K C, LAI M C, PENG C W , et al. Comparative studies on the corrosion protection effect of DBSA-doped polyaniline prepared from in situ emulsion polymerization in the presence of hydrophilic Na +-MMT and organophilic organo-MMT clay platelets [J]. Electrochimica Acta, 2006,51(26):5645-5653.
[8]	XIE H Q, MA Y M, GUO J S . Conductive polyaniline-SBS composites from in situ emulsion polymerization[J]. Polymer, 1999,40(1):261-265.
[9]	刘谊军, 杜玉成, 王会元 , 等. 聚苯胺防腐导电涂料的制备研究[J]. 涂料工业, 2007,37(6):16-18.
[10]	易波, 王群, 郭红霞 . 聚苯胺/环氧树脂防静电涂料的研制[J]. 化工新型材料, 2010,38(6):112-114.
[11]	MALMONGE J A, SANTOS M A, SAKAMOTO W K . Analysis of dipolar relaxation in polyurethane/polyaniline blend[J]. Journal of Materials Science, 2005,40(17):4557-4560.
[12]	YANG S M, LEE H L . The Conductivity and morphology of the blend of polyaniline and water based polyurethane[J]. Synthetic Metals, 1999,102(1-3):1226-1227.
[13]	廖梓珺, 晏华, 陈国需 , 等. 硅烷偶联剂对聚苯胺/钛酸钡复合粒子的结构影响[J]. 功能材料, 2007,38(11):1820-1823.

[1]	MA Y B, LIU B L, MA Y J, et al. Preparation and Properties of Ultralight Hollow Polymer Microspheres for Thermal Insulation Coatings [J]. Paint & Coatings Industry, 2025, 55(5): 53-59.
[2]	XIA X L, LOU Y P, LI D Z, et al. Synthesis and Properties of Vinyl-terminated Graphene Oxide and Carbon Nanotube Composite Polyurethane UV Resins [J]. Paint & Coatings Industry, 2025, 55(2): 32-37.
[3]	BAN L L, ZHAO Y X, ZHANG S, et al. Properties of functionalized boron nitride UV-curable thermal conductive coating [J]. Paint & Coatings Industry, 2024, 54(7): 8-15.
[4]	PAN H M, DONG Q F, YANG L F, et al. Research progress of intrinsic thermal conductive insulating liquid crystal epoxy resin [J]. Paint & Coatings Industry, 2024, 54(6): 82-88.
[5]	REN Y P, XING B Y, LI S J, et al. Preparation and Application of Graphene Enhanced Epoxy Thermal Conductivity Coating [J]. Paint & Coatings Industry, 2024, 54(5): 66-70.
[6]	GAO P, XUE Z W, GAO M M, et al. Preparation and Research of Low Density Polyvinyl Chloride Sealant for Robot [J]. Paint & Coatings Industry, 2024, 54(2): 50-55.
[7]	QIN Y, XUE G M, XU J, et al. Research and Application Progress of Graphene-based Electrothermal Coatings [J]. Paint & Coatings Industry, 2024, 54(12): 80-84.
[8]	LI X, SUN Z H, LI J Y, et al. Preparation and Properties of Bisphenol A Type Phenolic Epoxy Resin and Coating Reinforced by Nano-SiO₂ [J]. Paint & Coatings Industry, 2023, 53(8): 20-25.
[9]	ZHAO N, HU Z W, CHEN Y J, et al. Research on the Preparation of Epoxy Phosphate Ester Resins and Their Application in the Field of Metal Corrosion Protection [J]. Paint & Coatings Industry, 2023, 53(6): 30-38.
[10]	CHEN X, LIN P Z, QI Y F, et al. Study on Tensile Properties and Constitutive Relation of Heavy-duty Anticorrosive Coatings for Steel Structures [J]. Paint & Coatings Industry, 2023, 53(11): 16-33.
[11]	Yuan TianXiao Renjie, Wang Liwei. Development of Solvent-Free Insulating Anticorrosive and Waterproof Coatings [J]. Paint & Coatings Industry, 2019, 49(8): 41-46.
[12]	Meng Xiaoming, Chen Shengnan, Du Ting, Wang Limin, Wu Hao, Chen Simin. Preparation and performance study of thermal dissipation coatings for bus bars [J]. Paint & Coatings Industry, 2019, 49(2): 71-77.
[13]	Jing Lin,Ping Lv,Weibo Huang,Mingliang Ma,Wenting Li. Study on Natural Aging Properties of Sprayed Polyurea and PU Protective Coatings [J]. Paint & Coatings Industry, 2018, 48(7): 57-61.
[14]	Jiaying Zhang. Research Progress of Graphene Modified Organic Anticorrosive Coatings [J]. Paint & Coatings Industry, 2018, 48(11): 72-78.
[15]	Shuili Lai,Chen Gao,Zhuan Liu,Ruiqi Wang. Preparation of Crosslinked Waterborne Polyurethane from Castor Oil Modified by Maleic Anhydride [J]. Paint & Coatings Industry, 2018, 48(10): 38-42.

Please choose a citation manager

Content to export