Study on Corrosion Behavior of Zn-Al-Mg Coating in 3.5%NaCl Solution

doi:10.12020/j.issn.0253-4312.2018.12.7

Abstract

Abstract:

In this paper, scanning electron microscopy and scanning probe are used to analyze the surface morphology and composition of the Zn-Al-Mg coating. X-ray photoelectron spectrometer and electrochemical technology are used to analyze the chemical composition and electrochemical property of the corrosion products on Zn-Al-Mg coating. The corrosion mechanism of Zn-Al-Mg coating are discussed. The conclusions are as follows: Zn-Al-Mg coating is mainly composed of primary phase, aluminium rich phase and eutectic composition. Mg elements are mainly distributed in the eutectic organization. In the process of corrosion, the corrosion products on Zn coating are mainly composed of Zn₅(CO₃)₂(OH)₆ and ZnO, and the corrosion products on Zn-Al-Mg coating are mainly composed of Mg(OH)₂,4MgCO₃·Mg(OH)₂ and Zn₅(CO₃)₂(OH)₆. The charge transfer resistance of corrosion products on Zn coating is gradually reduced while the charge transfer resistance of the corrosion products on Zn-Al-Mg coating is gradually increased, and the latter is greater than the former. The corrosion products of zinc coating can not inhibit the corrosion of the coating while the corrosion products of zinc aluminum and magnesium can inhibit the electrochemical reaction of the coating and provide corrosion protection to the coating.

Key words: Zn-Al-Mg coating, corrosion products, chemical composition, corrosion resistance

摘要：

使用扫描电镜及扫描探针分析了锌铝镁镀层的表面形貌及成分,使用X射线光电子能谱仪及电化学技术分析了锌铝镁镀层腐蚀产物的化学组成、电化学性能,对锌铝镁镀层的耐蚀机制进行了探讨,结果表明:锌铝镁镀层主要由初生锌相、富铝相及共晶组织组成,Mg元素主要分布于共晶组织中。在3.5%NaCl介质腐蚀过程中,锌镀层腐蚀产物主要由Zn₅(CO₃)₂(OH)₆及ZnO组成,锌铝镁镀层腐蚀产物主要由Mg(OH)₂、4MgCO₃·Mg(OH)₂及Zn₅(CO₃)₂(OH)₆组成。锌镀层腐蚀产物电荷传输电阻逐渐降低,而锌铝镁镀层腐蚀产物电荷传输电阻逐渐增大,且后者大于前者。即锌镀层腐蚀产物无法抑制镀层的腐蚀,而锌铝镁镀层腐蚀产物则可以对镀层电化学反应起到抑制作用,对镀层提供一定程度的保护。

关键词: 锌铝镁镀层, 腐蚀产物, 化学组成, 耐蚀性

CLC Number:

TQ630.4

Yulin Hao,Hai Shen,Yi Zhao. Study on Corrosion Behavior of Zn-Al-Mg Coating in 3.5%NaCl Solution[J]. Paint & Coatings Industry, 2018, 48(12): 7-15.

郝玉林,生海,赵一. 锌铝镁镀层于3.5%NaCl溶液中腐蚀行为的研究[J]. 涂料工业, 2018, 48(12): 7-15.

/ / Recommend / Download Citations

URL: https://www.cn-pci.com/EN/10.12020/j.issn.0253-4312.2018.12.7

https://www.cn-pci.com/EN/Y2018/V48/I12/7

References

[1]	赵安伟 . 涂装车身喷蜡防腐分析探讨[J]. 上海涂料, 2013,51(1):35-37.
[2]	宋华, 宫金宝, 于泽淼 . 汽车防腐蚀应对措施及涂层耐腐蚀性能评价[J]. 汽车工艺与材料, 2015 ( 11):21-25.
[3]	李锋, 吕家舜, 杨洪刚 , 等. 锌铝镁镀层在 NaCl 体系中的腐蚀行为[J]. 中国表面工程, 2011,24(4):25-29.
[4]	李锋, 吕家舜, 杨洪刚 , 等. 锌铝镁镀层钢板的研究进展[J]. 轧钢, 2013 ( 2):45-51.
[5]	杨洪刚, 李锋, 吕家舜 . Z1. 6A1. 6M 合金镀层组织结构及性能研究[J]. 鞍钢技术, 2014 ( 1):38-41.
[6]	VOLOVITCH P, VU T N , ALLéLY C , et al. Understanding corrosion via corrosion product characterization: II. Role of alloying elements in improving the corrosion resistance of Zn-Al-Mg coatings on steel[J]. Corrosion Science, 2011,53(8):2437-2445.
[7]	DAN P, THIERRY D, LEBOZEC N , et al. In situ, infrared reflection spectroscopy studies of the initial atmospheric corrosion of Zn-Al-Mg coated steel[J]. Corrosion Science, 2013,72(72):54-63.
[8]	AZEVEDO M S, ALLéLY C, OGLE K , et al. Corrosion mechanisms of Zn(Mg, Al) coated steel in accelerated tests and natural exposure: 1. The role of electrolyte composition in the nature of corrosion products and relative corrosion rate[J]. Corrosion Science, 2015,90:472-481.
[9]	VIMALANANDAN A, BASHIR A, ROHWERDER M . Zn-Mg and Zn-Mg-Al alloys for improved corrosion protection of steel: some new aspects[J]. Materials & Corrosion, 2014,65(4):392-400.
[10]	VOLOVITCH P, ALLELY C, OGLE K . Understanding corrosion via corrosion product characterization: I. Case study of the role of Mg alloying in Zn-Mg coating on steel[J]. Corrosion Science, 2009,51(6):1251-1262.
[11]	DILER E, ROUVELLOU B, RIOUAL S , et al. Characterization of corrosion products of Zn and Zn-Mg-Al coated steel in a marine atmosphere[J]. Corrosion Science, 2014,87(6):111-117.
[12]	LEBOZEC N, THIERRY D, ROHWERDER M , et al. Effect of carbon dioxide on the atmospheric corrosion of Zn-Mg-Al coated steel[J]. Corrosion Science, 2013,74(4):379-386.
[13]	KEPPERT T A, LUCKENEDER G, STELLNBERGER K H , et al. The effect of sulphate, phosphate, nitrate and acetate on the corrosion behaviour of Zn Al-Mg hot-dip galvanised steel[J]. Materials & Corrosion, 2014,65(6):560-568.
[14]	STOULIL J, PROSEK T, NAZAROV A , et al. Electrochemical properties of corrosion products formed on Zn-Mg, Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions[J]. Corrosion Science, 2014,86(8):231-238.
[15]	生海, 郝玉林, 刘兴全 , 等. 组织结构对锌-铝-镁合金热浸镀层耐蚀性的影响[J]. 电镀与涂饰, 2017(5):239-242.
[16]	YAO C, TAY S L, ZHU T , et al. Effects of Mg content on microstructure and electrochemical properties of Zn-Al-Mg alloys[J]. Journal of Alloys & Compounds, 2015,645:131-136.
[17]	DUCHOSLAV J, STEINBERGER R, ARNDT M , et al. Evolution of the surface chemistry of hot dip galvanized Zn-Mg-Al and Zn coatings on steel during short term exposure to sodium chloride containing environments[J]. Corrosion Science, 2015,91:311-320.
[18]	HOSKING N C, STRÖM M A, SHIPWAY P H , et al. Corrosion resistance of zinc-magnesium coated steel[J]. Corrosion Science, 2007,49(9):3669-3695.
[19]	DILER E, RIOUAL S, LESCOP B , et al. Chemistry of corrosion products of Zn and MgZn pure phases under atmospheric conditions[J]. Corrosion Science, 2012,65:178-186.

Please choose a citation manager

Content to export