摘要： 采用相反转法制备水性醇酸树脂乳液，探究搅拌速度、加水速度、乳化温度等工艺条件对乳液制备产生的影响。结果表明：乳化剂加量 5%，200^#溶剂油加量为 3%，搅拌速度 4 000~ 6 000 r/min，加水速度 90~120 mL/h，乳化温度 50~60 ℃，KOH加量为 0.5%时所制备的乳液粒径 D₉₀≤ 307 nm，乳液稳定性，涂膜各项性能均达到相关国标要求。

关键词: 醇酸树脂乳液, 相反转法, 稳定性

Abstract: The title aqueous alkyd resin emulsion was prepared by phase inversion process，and the influence of stirring speed，addition rate of water and the emulsification temperature on the preparation of emulsion were investigated. The results showed that thefavorite emulsification condition was as follows：the emulsifier level，200^# solvent，and KOH were 5%，3%，and 0.5%，respectively，the stirring speed between 4000 and 6000r/min，the addition rate of water adding 90~120mL/h，and emulsification temperature 50~60 ℃. The particle size of the emulsion D₉₀≤307 nm. The stability of the emulsion and other properties ofthe coatings film met the relevant national standards.

Key words: alkyd resin emulsion, phase inversion process, stability