A novel epoxy putty was prepared through polyurethane modified epoxy resin and mixed a-mines. It was found that the putty, besides its usual good corrosion resistance, chemical resistance and adhe-sion, has good tensile performance, the yield elongation was over 8%.
Key words:
modified epoxy resin,
epoxy putty,
yield elongation,
pull off adhesion,
tensile strength
摘要： 以多异氰酸酯改性的环氧树脂与混合胺制备了新型环氧胶泥，此胶泥既具有常规环氧胶泥的防腐性、耐 化学品性以及优异的附着力，又具有厚填充时良好的拉伸性能，扯断伸长率达到 8%以上。
关键词:
改性环氧树脂 ,
环氧胶泥 ,
扯断伸长率 ,
拉开法附着力 ,
拉伸强度
Jin Jiahong, Zhang Xiugin', Yang Yongbing, Lu Zhefang, wang suqin. Development and Application of Novel Epoxy Putty[J]. Paint & Coatings Industry, 2009, 39(4): 26-27.