摘要： 采用芘荧光探针，通过对比分析芘第一振动峰（I1，373nm处）和第三振动峰（I3，384nm处）的荧光强度之比（I1/I3）在不同乳化剂配比［m（AS）∶m（OP）］、乳化剂用量、引发剂用量及 pH条件下的变化规律，利用其斜率的绝对值｜K｜表征了聚合反应速率，并结合单体转化率，对丙烯酸酯乳液聚合工艺进行了优化。研究结果显示：当乳化剂配比、乳化剂用量、引发剂用量及 pH分别为 2∶1（质量比）、5%（占单体总质量的质量分数，下同）、0.7%及 pH＝3时，得到的乳液具有优良的综合性能，表明荧光探针技术可用于优化丙烯酸酯乳液的聚合工艺。
关键词:
荧光探针技术,
丙烯酸酯乳液,
聚合工艺
Abstract: Relationships between the ratio of composite emulsifiers, amounts of composite emulsifiers, amounts of initiator(KPS), PH values and the intensity ratio of the first ns. the third peak(I1/I3)in the fluorescence spectrum of pyrene were discussed during the emulsion polymerization process. The optimization of polymerization reaction of acrylic emulsion were completed effectively by analyzing the absolute value of the slope of I1/I3(|K|)and the conversion. The experimental results revealed that a good performance emulsion was obtained while m(AS): m(OP)=2: 1, the mass ratio of composite emulsifier us. monomer was 5%, the mass ratio of initiator us. monomer was 0.7%, and pH=3 respectively. Therefore, the pyrenyl probes can be effectively used to optimize the polymerization process of acrylic emulsion.
Key words:
fluorescence probe technique,
acrylate emulsion,
polymerization process
马 利, 贾春悦, 甘孟瑜, 郝少娜, 谷静莲, 李志春, 刘兴敏. 荧光探针法优化丙烯酸酯乳液聚合工艺[J]. 涂料工业, 2011, 41(8): 4-8.
Ma Li, Jia Chunyue, Gan Mengyu, Hao Shaona, Gu Jinglian, Li Zhichun, Liu Xingmin. Application of Fluorescence Probe Technique in the Optimization of Polymerization Reaction of Acrylic Emulsion[J]. Paint & Coatings Industry, 2011, 41(8): 4-8.