A water-in-water（w/w） multicolor coatings with excellent comprehensiveproperties was prepared based on the hydrophilic isocyanateas curing agent，lithium magnesium silicate as protective glue，combination of dispersed hydroxyl acrylic resin andelastic polyacrylic latex as dispersed phase，and by using the gelation reaction betweeninterlayer exchangeable cations in lithium magnesium silicate and hydroxyl groups inhydroxyethyl cellulose and the cross-linking of hydroxyl resin and hydrophilic curing agent.The experimental results showed that when the blending ratio of dispersion and latex was 1∶4， —NCO curing agent and —OH component was 1∶2（by molar ratio），and the bleeding was 4% with high concentration protective glue，the obtained color particles was characterized by its moderate stiffness，high color strength，and better color bleeding resistance，as well as goodapplicability without sagging and good storage stability.Some problems of the w/w multicolorcoatings during production and application，such as bleeding，easy breakage of color particles and unevensurface after spraying were solved.
PANG Jiang
,
MAO Wei-Jie
. Study on the Stability of Color Particle of Texture W/W Multicolor Coatings[J]. Paint & Coatings Industry, 2019
, 49(9)
: 14
-20
.
DOI: 10.12020/j.issn.0253-4312.2019.9.14
[1]戴志浩，胡中源，于占江.凝胶型水包水多彩外墙涂料的探讨[J].中国涂料, 2013, 28(9):48-52
[2]王晓，侯佩民，徐元浩，等.水包水多彩涂料发展概况[J].中国涂料, 2012, 27(8):23-26
[3]潘红霞.水性多彩涂料的研发及应用[J].上海涂料, 2013, 51(12):10-13
[4] INOUET，OZAKI T，ADACHI J，et al.Aqueous multicolor coating composition：WO2012147693A1 [P]. 2012-11-01.
[5]RODRIGUEZ R，CAROLINA D L H A，EKANAYAKE P， et al.Correlation of silicone incorporation into hybrid acryliccoatings with the resulting hydrophobic and thermal properties[J].Macromolecules, 2008, 41(22):8537-8546
[6]崔航，王峰，胡剑青，等.水包水型仿花岗岩多彩涂料的研究进展[J].涂料工业, 2016, 46(3):75-78
[7]朱若君 .凝胶型水包水多彩涂料稳定性能研究 [D].重庆：重庆大学， 2015.
[8]李湘祁，林辉 .饰面石材加工基础 [M].北京：中国建材工业出版社， 2016.
[9]徐冬，黄凯，乔永洛，等.水包水多彩涂料用基础漆乳液的制备及应用研究[J].涂料工业, 2017, 47(1):61-67
[10]HUYBRECHTS J，BRUYLANTS P，VAES A，et al.Surfactant-free emulsions for waterborne，two-component polyurethanecoatings[J].Progress in Organic Coatings, 2000, 38(2):67-77
[11]NOBLE K. Waterborne polyurethane[J].[J].Progress in OrganicCoatings, 1997, 32:131-136
[12] MOY W.Aqueous multicolor paint with improved solvent re.sistance：WO2004046261A2 [P]. 2004-06-15.
[13] LAAS H， HALPAAP R.Modified polyisocyanates： US2004034162A1 [P]. 2004-02-19.
[14]陈鹏，刘建明.交联剂对水性双组分聚氨酯漆性能的影响[J].涂料工业, 2002, 32(7):9-11
[15]余喜红，任娜娜，李红星，等.双组分水性聚氨酯涂膜交联密度的研究[J].涂料工业, 2010, 40(1):38-43
[16]钱蕴 .单交联体系水性仿石涂料凝胶粒子的制备与研究[D].北京：北京化工大学， 2010.