Three graphene oxides with different degrees of oxidation were prepared，which were used to modify the epoxy zinc-based coatings. The properties of the modified coatings were studied by salt spray test，electrochemical test，impact resistance and adhesion test. The results showed that the graphene oxide modified epoxy zinc-based coatings with lower oxidation degree provided the best performance. The effects of the content of graphene oxideand zinc powder on the corrosion resistance and mechanical properties of the coatings were investigated.
The results showed that the addition of graphene oxide could effectively delay the corrosion of steel，when the amount of GO-1 added was 0.36% and the content of zinc powder was 44%， the overall performance of the prepared GO-1/waterborne epoxy zinc-based coating was the
best. When the graphene oxide is less oxidized，the less of oxygen-containing groups，and the carboxyl group was not existed，the corrosion resistance of the coating was improved.
CHEN Zhong-Hua
,
LI Qing
. Effects of the Oxidisation Degree and Content of Graphene on the Anticorrosion Properties of Waterborne Zinc-Based Coatings[J]. Paint & Coatings Industry, 2019
, 49(6)
: 35
-41
.
DOI: 10.12020/j.issn.0253-4312.2019.6.35
[1]LIANGK，CHAO G.Making silica nanoparticle－covered graphene oxide nanohybrids as general building blocks forlarge-area superhydrophilic coatings[J].Nanoscale, 2011, (3):519-528
[2]SONYW，COHEN M L，LOUIE S G.Half -metallic graphene nanoribbons[J].Nature, 2006, 444(7117):347-349
[3]赵振涌，陈玲，钟洁.石墨粉对低锌含量水性环氧富锌底漆阴极保护性能的影响[J].电镀与涂饰, 2014, 33(18):774-777
[4]王清海，王秀娟，方健君，等.石墨烯在环氧富锌底漆中的应用[J].涂料工业, 2016, 46(12):42-47
[5]薛鹏，李文凯，胡秀东，等 .石墨烯浆料在环氧锌粉复合防腐涂料中的应用 [J]．涂料工业， 2017，47（11）59-63.
[6]万雪期，姚伟，郭翠翠，等 .氧化石墨烯 /环锌底漆的制备及性能研究 [J].涂层与防护， 2018，39（1）30-35.
[7]张松 .石墨烯 /水性环氧富锌涂料的制备及性研究 [D].哈尔滨：哈尔滨工业大学， 2017.
[8]王舟 .环氧树脂 /氧化石墨烯纳米复合材料的制备与表征[D].北京：北京化工大学， 2010.
[9]李洪飞，王华进，扈中武 .氧化石墨烯在膨胀型水性防火涂料中阻燃和抑烟作用研究 [J].涂料工业， 2015，45（1）1-8.
[10]李拯 .氧化石墨烯 /环氧树脂复合材料的界面改能研究 [D].哈尔滨：哈尔滨工业大学， 2013.