制备了一种低气味、低温塑化型聚氯乙烯抗石击涂料，主要探讨了增塑剂、糊树脂，附着力促进剂对试样气味、弯曲性、附着力等性能的影响。实验结果表明：采用对苯二甲酸二异壬酯与烷基磺酸酯作为混合增塑剂，能够降低气味的同时满足低温塑化后的柔韧性要求；维尼泰 370HD糊树脂具有较好的黏度稳定性，并且作为主树脂改善涂料的流淌性；采用阿科玛 PA1384共聚树脂作为辅助糊树脂，喷涂扇幅受影响较小，可提高低温塑化后的涂层拉伸强度；采用 N382附着力促进剂不仅涂料气味较低，而且低温塑化后附着力较好。
A low-odor，low-temperature plasticized polyvinyl chloride chip-resistant coatings was prepared. The effects of plasticizer，paste resin and adhesion promoter on sample odor，bending and adhesion were studied. The results showed that diisononyl terephthalate andphenyl alkyl sulfonate were used as the mixed plasticizers，which could reduce the odor and meet the requirements of flexibility after low temperature plasticization. Siamvic 370HD pasteresin provided good viscosity stability，and used as the main resin to improve the flow of coatings；PA1384 copolymer resin from Arkema was used as auxiliary resin，and the spray width was less affected，which could improve the tensile strength of the coatings after lowtemperature plasticization. N382 adhesion promoter showed not only lower odor，but also better adhesion after low temperature plasticization.
[1] 邹志群 .汽车用新型 PVC抗石击涂料的制备及性能研 究[D].广州：华南理工大学， 2015.
[2]刘成楼.车辆防腐防石击底漆的研制[J].上海涂料, 2013, 51(9):1-2
[3] 张彦素 .聚氨酯系汽车车底防石击涂料的研究 [D].长沙：国防科学技术大学， 2007.
[4]蒋清华.汽车保护用可湿碰湿聚氯乙烯涂料的研究[J].上海涂料, 2005, 43(4):11-13
[5]杨磊.高发泡型汽车车底抗石击涂料应用研究[J].现代涂料与涂装, 2016, 19(3):22-24
[6]昌福全.特种涂料在汽车涂装中的应用[J].中国涂料, 2005, 20(11):42-43
[7]陈坤，时爽，唐强，等.纳米碳酸钙在汽车抗石击涂料中的应用[J].应用化工, 2018, 47(3):559-562
[8]WANGGQ，WANG Y H，ZOU H K，et al.Rheological andgelation properties of PVC paste filled with nanometerCaCO3[J].Plastics Science and Technology, 2000, (5):15-17
[9]匡正，惠畅，项尚林，等.低温塑化型 塑熔胶用封端聚氨酯的研制[J].中国胶粘剂, 2009, 18(10):15-18