针对钢厂煤气管道使用过程存在内壁腐蚀和黏结粉尘问题，以气相二氧化硅、碳化硅、胶体石墨、鳞片石墨烯和有机硅聚合物改性液体树脂为原料，采用溶胶-凝胶法制备了有机硅聚合物改性液体树脂-无机填料复合涂料，研究了涂层的润湿性、机械强度、防腐蚀和防结垢性能。结果表明：涂层具有良好的疏水性，表面能为 25. 91 mJ/m²，相比碳钢降低了 41. 58%，水接触角为 120. 1 °；附着力 1级且几乎不受温度变化的影响；经砂纸磨损后，涂层的水接触角仍大于 105 °，展现出良好的耐磨性；在硫酸、盐酸和氯化钠溶液中的最大腐蚀速率分别为 12. 36 mg/（cm².h）、9. 89 mg/（cm2.h）和 2. 55 mg/（cm².h），相比碳钢分别降低了 73%、74%和 83%；同时，涂层能有效抑制 NH₄Cl的结晶黏结。在工业现场煤气管道中进行连续 5个月防腐蚀和防结垢性能应用测试，相比普通碳钢，涂装涂料的管道表面没有出现明显的腐蚀与结垢行为。气相二氧化硅分子在涂层表面形成了具有疏水性的微纳米结构，填料之间相互重叠形成了类似“迷宫”的结构，以及胶体石墨与碳化硅的协同作用是该涂料表现出优异的防腐蚀防结垢性能的机理。

Aiming at the issues of internal wall corrosion and adhesive dust in steel plant gas pipelines，a silicon polymer modified liquid resin-inorganic filler composite coating was prepared by sol-gel method using fumed silica，silicon carbide，colloidal graphite，flake graphene and silicon polymer modified liquid resin as raw materials. The wettability，mechanical strength，anticorrosive and anti-scaling properties of the coating were studied. The results showed that the coating exhibited，the surface energy was 25. 91 mJ/m²，which was 41. 58% lower than that of carbon steel，and the contact angle was 120. 1 °，exhibiting excellent hydrophobicity. The adhesion strength was grade 1，and almost unaffected bytemperature variations. The water contact angle remained greater than 105 ° after sandpaperabrasion，demonstrating good wear resistance. The maximum corrosion rates in sulfuric acid， hydrochloric acid and sodium chloride solutions were 12. 36 mg/（cm².h），9. 89 mg/（cm².h）， and 2. 55 mg/（cm².h），respectively，which was 73%，74%，and 83% lower than that of carbon steel. Additionally，the coating could effectively inhibit the crystallization and adhesion of NH₄Cl. There were no significant corrosion or scaling was observed on the coated pipelinesurfaces in a five-month continuous corrosion and scaling resistance application test. Benefiting from the hydrophobic micro-nano structure formed by fumed silica molecules oncoating surface，"maze-like" structure created by the overlapping fillers，and the synergistic effects of colloidal graphite and silicon carbide，the coating showed excellent anticorrosive and anti-scaling properties.