采用油酸对商用二氧化钛进行表面改性，通过 X-射线光电子能谱仪（ XPS）、红外光谱（FT-IR）和 X射线粉末衍射分析（ XRD）对改性后的 TiO2粒子进行了结构表征，并借助热重分析测定了改性剂的含量。采用光差示扫描量热法（ photo-DSC）研究了无机膜保护型 TiO2、去包膜型 TiO2、油酸改性 TiO2和三甲基苯甲酰二苯基氧化膦（ TPO）对丙烯酸酯光聚合动力学的影响。结果表明：油酸改性的 TiO2与无机膜保护的 TiO2和去包膜的 TiO2相比，能在空气中引发丙烯酸酯的光聚合，并能增强以 TPO为光引发剂的丙烯酸酯的光聚合，从而在相同固化效果下，可减少小分子光引发剂的添加，降低残留。本研究为后续紫外光（UV）固化白色涂料、油墨固化不完善等问题提供了解决途径。
The surface of commercial titanium dioxide was modified by oleic acid. The surface structure of modified titanium dioxide particles was characterized by X-ray photoelectron spectroscopy（XPS）， infrared spectroscopy（FT-IR） and X-ray diffraction analysis（XRD）. The amount of oleic acid immobilized on TiO2 particle was determined bythermogravimetric analysis. The influence on photopolymerization kinetics of acrylate were evaluated with Photo-DSC，including the inorganic coated TiO2，coat removed TiO2，oleic acid modified TiO2 and trimethylbenzoyl diphenylphosphine oxide（TPO）， respectively. It was shown that the oleic acid modified TiO2 could substantially initiate photopolymerization of acrylate under air，compared to the inorganic coated TiO2 or coat removed TiO2，and also enhanced the photopolymerization of acrylate with TPO as photoinitiator，while reduced addition of small molecule photoinitiator and reduced the residue at the same curing degree.This study provided further solutions to the problems such as the incomplete curing of white coatings and inks cured by ultraviolet .
[1]陈用烈，曾兆华，杨建文 .辐射固化材料及其应用 [M].北京：化学工业出版社， 2003：130-140.
[2]杨建文，梁红波，包芬芬 .辐射固化技术研究进展 [M].北京：中国科学技术出版社， 2018：254-282.
[3]肖勇丽.钛白粉在涂料中的应用概述[J].四川冶金, 2014, (1):9-13
[4]MILLSA，HUNTE S L.An overview of semiconductor photocatalysis[J].Journal of Photochemistry and Photobiology A：Chemistry, 1997, 108(1):1-35
[5]STRANDWITZ N C，NONOGUCHI Y，BOETTCHER S W， et al.In situ photopolymerization of pyrrole in mesoporousTiO2[J].Langmuir, 2010, 26(8):5319-5322
[6]NIX，YE J，DONG C.Kinetics studies of methyl methacry-late photopolymerization initiated by titanium dioxide semiconductor nanoparticles[J].Journal of Photochemistry& Photobiology A：Chemistry, 2006, 181(1):19-27
[7]KRAEUTLER B，REICHE H，BARD A J，et al.Initiation of free radical polymerization by heterogeneous photocatalysisat semiconductor powders[J].Journal of Polymer SciencePart C Polymer Letters, 1979, 17(8):535-538
[8]YEJ，NI X，DONG C.Electric charge scavenger effects inPMMA photopolymerization initiated by TiO2 semiconductor nanoparticles[J].Journal of Macromolecular Science Part A： Pure and Applied Chemistry, 2005, 42(10):1451-1461
[9]KAZEMI F，MOHAMADNIA Z，KABOUDIN B，et al.Synthesis and characterization of maleylated cellulose-g-polyacrylamide hydrogel using TiO2 nanoparticles under sunlight[J].Iranian Polymer Journal, 2017, 26(9):663-672
[10]ZHANG W，YUAN Z，HUANG L，et al. Titanium dioxide photocatalytic polymerization of acrylamide for gel electropho-resisof proteins and structural identificationby mass spectrometry[J].[J].Scientific Reports, 2016, 6:20981-
[11]GLASS S，TRINKLEIN B，ABEL B，et al. TiO2 as photosensitizer and photoinitiator for synthesis of photoactiveTiO2-PEGDA hydrogel without organic photoinitiator[J].[J].Frontiers in Chemistry, 2018, 6:340-
[12]HOFFMAN A J，MILLS G，YEE H，et al.Q-sized cadmium sulfide： synthesis， characterization， and efficiency of photoinitiation of polymerization of several vinylic monomers[J].Cheminform, 1992, 23(40):5021-5036
[13]WENG Z，NI X，YANG D，et al. Novel photopolymerizationsinitiated by alkyl radicals generated from photocatalyzeddecarboxylation of carboxylic acids over oxide semiconductornanoparticles：extended photo-Kolbe reactions[J].[J].Journalof Photochemistry and Photobiology A Chemistry, 2009, 201 2-3:151-156
[14]YE J，NI X，DONG C.Electric charge scavenger effects in PMMA photopolymerization initiated by TiO2 semiconductor nanoparticles[J].Journal of Macromolecular Science Part A： Pure and Applied Chemistry, 2005, 42(10):1451-1461
[15]张娜 .氧杂环丁烷 -甲基丙烯酸酯杂化单体的合成及光聚合动力学研究 [D].北京：北京化工大学， 2018.
[16]WANG L Q，FERRIS K F，SHULTZ A N，et al.Interactions of HCOOH with stoichiometric and defective TiO2(110)surfaces[J].Surface Science, 1997, 380(2-3):352-364
[17]MARTRA G，COLUCCIA S，MARCHESE L，et al.The role of H2O in the photocatalytic oxidation of toluene in vapour phase on anatase TiO2 catalyst：a FTIR study[J].Catalysis Today, 1999, 53(4):695-702
[18]GRINTER D C，WOOLCOT T，PANG C L，et al.Ordered carboxylates on TiO2(110)formed at aqueous interfaces[J].Journal of Physical Chemistry Letters, 2014, 5(24):4265-4269
[19]DEACON G B，PHILLIPS R J，DEACON G B.Relationships between the carbon-oxygen stretching frequencies of carboxylato complexes and the type of carboxylate coordination[J].Coordination Chemistry Reviews, 1980, 33(3):227-250
[20]NAMPOOTHIRI P K，GANDHI M N，KULKARNI A R. Elucidating the stabilizing effect of oleic acid coated LaF3：Nd3+，nanoparticle surface in the thermal degradation of PMMA nanocomposites[J].[J].Materials Chemistry and Physics, 2017, 190:45-52