为了消除有机光引发剂在光解时产生的小分子污染物，制备了纳米氧化锌，并合成了水性聚氨酯丙烯酸酯，按照一定的比例，将纳米氧化锌作为光引发剂，制得无机纳米光引发剂引发的水性光固化涂料。采用红外光谱仪、紫外可见分光光度计、 X-射线衍射仪、马尔文粒度仪、透射电子显
微镜、热重分析仪、扫描电子显微镜等测试分析了纳米氧化锌与水性光固化聚氨酯丙烯酸酯的漆膜；同时研究了漆膜的物理性能，当纳米氧化锌的添加量为 1%时，光固化漆膜的硬度为 H、附着力为 0级、光泽为 90左右、耐水性良好、耐碱性能好、耐醇性优良。表明纳米氧化锌可以代替有机光引发剂，用于水性光固化聚氨酯丙烯酸酯，从而合成出更环保、更优良的水性光固化涂料。
In order to eliminate the small molecular fragments generated by organicphotoinitiators during photolysis，nano zinc oxide was prepared and waterborne polyurethaneacrylates was synthesized. Nano zinc oxide with a certain weight percentage was used as aninorganic photoinitiator for waterborne UV-curable coatings. The nano zinc oxide and UV-curedfilms of waterborne UV-curable coatings were analyzed by infrared spectroscopy，ultraviolet spectroscopy，X-ray diffraction，Malvern particle size analyzer，Zeta potential，transmission electron microscopy，thermogravimetric analysis，and scanning electron microscopy，respectively. Themechanical and physical properties of the paint film were also tested. When the content of nano-zinc oxide is 1%，the UV-cured film provided a hardness of H，adhesion of grade 0，gloss of about 90，and good water resistance，alkali resistance and excellent ethanol resistance. It was demonstrated that nano zinc oxide could be used as an alternative photoinitiator to organicphotoinitiators for waterborne UV-curable polyurethane acrylates，making the waterborne UV-curable coatings more environmental friendly and better quality.
[1]邓锡柱，叶代勇.高固体分水稀释型聚氨酯丙烯酸酯黏度的影响因素[J].化工学报, 2016, 67(4):1586-1593
[2]魏杰，金养智 .光固化涂料 [M].北京：化学工业出版社， 2005.
[3] SCHWALM R.UV Coatings：basics，recent developments and new applications[M]. Amsterdam：Elsevier Science，2006.
[4] FOUASSIER J P，LALEVéE J P.Photoinitiators for polymer synthesis：scope，reactivity，and efficiency[M]. Weinheim： Wiley-VCH Verlag & Co. KGaA，2012.
[5]冯钦，方田，邓锡柱，等.改性光引发剂和优化光固化工艺制备低 涂料[J].涂料工业, 2016, 46(12):29-35
[6]SCHMITT M.Synthesis and testing of ZnO nanoparticles forphoto -initiation：experimental observation of two differentnon-migration initiators for bulk polymerization[J].Nanoscale, 2015, 7(21):9532-9544
[7]FENG J，FANG L，YE D. Self-photoinitiated oligomers ofwater-diluted polyurethane acrylate grafted with zinc oxideof low concentrations[J].[J].Progress in Organic Coatings, 2018, 120:208-216
[8]ELSAEEDAM，EL-FATTAH M A，AZZAM A M. Synthesisof ZnO nanoparticles and studying its influence on the anti-microbial，anticorrosion and mechanical behavior of poly-urethane composite for surface coating[J].[J].Dyes and Pig-ments, 2015, 121:282-289
[9]LIJH，HONG R Y，LI M Y，et al.Effects of ZnO nanoparticleson the mechanical and antibacterial properties of polyure-thane coatings[J].Progress in Organic Coatings, 2009, 64(4):504-509
[10]MALUCELLIA G，FIORAVANTI A，FRANCIOSO L，et al. Preparation and characterization of UV-cured composite filmscontainingZnO nanostructures：Effect of filler geometric featureson piezoelectric response[J].[J].Progress in Organic Coatings, 2017, 109:45-54
[11]MARKHAM M C，LAIDLER K J.A kinetic study of photo-oxidations on the surface of zinc oxide in aqueous suspen-sions[J].The Journal of Physical Chemistry B, 1953, 57(3):363-369
[12]HARBOUR J R，HAIR M L.Radical intermediates in the photosynthetic generation of hydrogen peroxide with aqueouszinc oxide dispersions[J].The Journal of Physical Chemis-try, 1979, 83(6):652-656
[13]HUANG Z Y，BARBER T，MILLS G，et al.Heterogeneousphotopolymerization of methyl methacrylate initiated by smallZnO particles[J].Journal of Physical Chemistry, 1994, 98(48):12746-12752
[14]HOFFMAN A J，YEE H，MILLS G，et al.Photoinitiated polymerization of methyl methacrylate using Q-sized ZnOcolloids[J].The Journal of Physical Chemistry, 1992, 96(13):5540-5546
[15]YAMAMOTO M，OSTER G.Zinc oxide-sensitized photopo-lymerization[J].Journal of Polymer Science Part A：Polymer Chemistry, 1966, 4(7):1683-1688
[16]DADASHI-SILAB S，ASIRI A M，KHAN S B，et al.Semi-conductor nanoparticles for photoinitiation of free radicalpolymerization in aqueous and organic media[J].Journal ofPolymer Science Part A：Polymer Chemistry, 2014, 52(10):1500-1507
[17]陈四海，任新民.纳米粒子的光物理性质 ──微量水对荧光的影响[J].影像科学与光化学, 1994, 12(3):268-272
[18]FENG J，YE D. Self-photoinitiating water-diluted polyure-thane acrylates and their UV-curing kinetics[J].[J].Progress inOrganic Coatings, 2019, 129:300-308
[19]DECKER C，MOUSSA K.Real-time kinetic study of laser-induced polymerization[J].Macromolecules, 1989, 22(12):4455-4462
[20] SCHMITT M.ZnO Nanoparticle-based photoinitiators[M]. London：Royal Society of Chemistry，2018：337-357.
[21]SCHMITT M，BECKER D，LALEVéE J. Performance analysisof the solidification of acrylic esters photo-initiated by sys-tematically modified ZnO nanoparticles[J].[J].Polymer, 2018, 158:83-89
[22] FOUASSIER J P.Photoinitiation，photopolymerization，and photocuring：fundamentals and applications[M]. Munich： Hanser-Gardner Publications，1995.
[23]黄萍，叶代勇.分子结构中碳碳双键对水性 聚氨酯分散体的影响[J].涂料工业, 2011, 41(10):48-53