针对水性重防腐涂层体系中水性环氧富锌底漆高锌粉含量所带来的生产成本高、不易贮存、环境污染大等问题，采用在涂料中添加少量石墨烯以取代部分锌粉的改进方法。通过动电位极化曲线、电化学阻抗谱等方法研究了锌粉含量以及石墨烯添加量对环氧富锌涂料性能的影响，结果表明：涂层的耐腐蚀性随着锌粉含量增加而提高，锌粉占锌粉与硫酸钡总质量的 80%时，腐蚀速率为 0. 002 03毫米 /年（ mm/y），当涂层中锌粉占锌粉与硫酸钡的总质量的 20%时，随着石墨烯添加量从占锌粉、硫酸钡与石墨烯总质量的 0增加至 0. 8%，腐蚀速率先上升后下降，当石墨烯含量达到 0. 6%时，腐蚀速率为 0. 0 038 mm/y，涂层的耐腐蚀性达到最大值。
Regarding the problems of high production cost，difficult storage and environmental pollution caused by the high zinc content in waterborne epoxy zinc-rich primer in the waterborne heavy-duty coating system，an improvement method of adding a small amount of graphene material to the coatings to replace part of the zinc powder was adopted. The effects of zinc powder content and graphene addition on the performance of epoxy zinc-rich coatings were investigated by means of potentiodynamic polarization and electrochemical impedance spectroscopy. It was shown that the corrosion resistance of the coatings increased with the increase of zinc powder content and when the content of zinc powder reach 80 wt%， the corrosion rate was 0.00203mm/y. The corrosion rate decreased first and then increased with the increase of graphene material content. When the content of Zn was 20 wt%，with a graphene material content of 0. 6 wt%，the corrosion resistance of the coatings reached the maximum and corrosion rate was 0. 0 038 mm/y.
[1]李彬 .水性环氧富锌防腐涂料研究[D].青岛：中国石油大学，2008.
[2]李善文，左彬，王刚，等.环氧富锌漆结霜副产物对涂层附着力的影响[J].现代涂料与涂装, 2015, 18(9):30-32
[3]刘光明，周街胜，王义元，等.改性水滑石的制备及对环氧富锌漆性能的影响[J].表面技术, 2017, 46(3):223-228
[4]张静星，李青山，王晓欣 .风电塔架水性防腐涂料的老化研究[C].锦州：全国红外加热暨红外医学发展研讨会论文集 . 2013.
[5]薛鹏，李文凯，胡秀东，等，石墨烯浆料在环氧锌粉复合防腐涂料中的应用[J].涂料工业，2017，47（11：）59-63.
[6]LIX，CAI W，AN J，et al.Large-area synthesis of high-quality and uniform graphene films on copper foils[J].Science, 2009, 324(5932):1312-1314
[7]NAIRRR，WU H A，JAYARAM P N，et al.Unimpededpermeation of water through helium-leak-tight graphene-based membranes[J].Science, 2012, 335(6067):442-444
[8]王书传，胡建林.石墨烯粉体在环氧锌粉底漆中的应用[J].涂料技术与文摘, 2017, 32(7):1-5
[9]孙春龙，关迎东.石墨烯在环氧锌粉涂料中的应用研究[J].中国涂料, 2017, 32(2):14-17
[10]关迎东，候晓燕，孙春龙.石墨烯-锌粉长效防腐涂料的研制[J].电镀与涂饰, 2017, (14):5-10
[11]薛鹏，李文凯，胡秀东，等.石墨烯浆料在环氧锌粉复合防腐涂料中的应用[J].涂料工业, 2017, (11):59-62
[12] MERMOUFEL A，DESLOUIS C，TOUZAIN S.Electro-chemical and anticorrosion performances of zinc-rich andpolyaniline powder coatings[J]. Electrochimica Acta，2008， 53（5）2331-2338.
[13]曹楚张鉴清.电化学阻抗普导论[M].北京：科学出版社, 2002, :-
[14] FANG Y H，LIU S，ZHAO W J，et al.Preparation andcorrosion resistance of graphene / fluorocarbon coating[J].Surface Technology，2016.
[15]谢卫红，杜红涛，季凯.纳米材料对水性涂层表面张力的影响[J].涂料工业, 2011, 41(2):37-41
[16]PANJL，WEN Y H，CHENG J，et al.Zinc deposition anddissolution in sulfuric acid onto a graphite-resin；compositeelectrode as the negative electrode reactions in acidic；zinc-based redox flow batteries[J].Journal of Applied Electro-chemistry, 2013, 43(5):541-551
[17] DING R，ZHENG Y，YU H，et al.Study of water permeationdynamics and anti-corrosion mechanism of graphene/zinccoatings[J]. Journal of Alloys and Compounds，2018： S0925838818310284.
[18]OSTROVSKY P M，GORNYI I V，MIRLIN A D.Conductivity of disordered graphene at half filling[J].European Physical Journal Special Topics, 2007, 148(1):63-72